關鍵詞：cbn contents hardness phase composition 

摘要：Well-sintered polycrystalline cubic boron nitride(PCBN)composites with different contents of cubic boron nitride(CBN) were obtained using Al and TiN as additives under pressure of 5.5 GPa and temperature of 1450 ℃.The network structure of CBN grains and bonding materials was observed using scanning electron microscope(SEM).With the help of X-ray diffraction(XRD) analysis,TiB2 and AlN could be determined as main products and Al3 Ti also was detected in the Al-rich samples after sintering process.Furthermore,it was shown that Vickers hardness of composites was improved with the increase of CBN contents.However,the lifetime of PCBN composites was in negative correlation with the amount of CBN in turning GCr15 hardened steels,and the surface roughness of workpieces machined by these PCBN composites also showed the same trend.A series of cutting data confirmed that the low CBN content in PCBN composites could enhance the working durability and improve the surface quality in turning hardened steels.The present experiments also indicated that the lowest value of flank wear was not constant for different PCBN composites when they were used to machine several workpieces with different hardness.

金剛石與磨料磨具工程雜志要求:

{1}引用資料非來自原始出處時，應注明“轉引自”。轉引文獻時，應先注明原始作品 之相關信息，再注明轉引所據之文獻。

{2}根據著作權法的有關規定，編輯部對來稿有權做文字性和技術性的修改、刪減。如有特殊情況請在稿件附言中注明。

{3}每篇論文應有200字左右的“摘要”，3-8個“關鍵詞”。摘要要求表達簡練，語義確切，結構嚴謹；應包括目的、方法、結果和結論；用第三人稱編寫；應反映論文的主要內容。

{4}作者姓名、性別、出生年、籍貫、民族、工作單位、職稱、學歷、研究方向。

{5}基金論文所涉及的課題如取得國家或部、省級以上基金項目，應腳注于文題頁左下方，作者單位上方，并附基金證書復印件，本刊將優先處理與刊登。

注：因版權方要求，不能公開全文，如需全文，請咨詢雜志社